Overview Summary
Create stronger, more refined 3D prints with the Anycubic PETG-CF Satin Carbon Fiber Filament 1kg in Black. Designed for FDM printers, this carbon fibre reinforced PETG filament delivers improved rigidity, impact resistance, a smooth satin texture and reliable performance for functional parts, prototypes and decorative models. Shop now and add advanced printing material to your 3D workflow.
With its weather-resistant properties and compatibility with hardened steel nozzles, this filament is suitable for demanding applications where strength and appearance matter. Buy now to produce detailed, durable prints with a professional finish.
Performance tier: Premium
Uses: functional prototypes, engineering parts, vehicle components, decorative models, toys, fandom creations Overview
Anycubic PETG-CF Satin Carbon Fiber Filament 1kg Black
The Anycubic PETG-CF Satin Carbon Fiber Filament 1kg in Black is engineered for FDM 3D printing enthusiasts and professionals who require stronger, more durable prints than standard PETG can provide. Reinforced with carbon fiber, this filament delivers enhanced rigidity, excellent impact resistance, and improved dimensional stability for demanding functional parts. Its satin finish naturally reduces the visibility of layer lines, giving printed models a cleaner, more premium appearance.
Designed for practical applications, this PETG-CF filament also offers reliable resistance to moisture and weather, making it suitable for components that may be exposed to more challenging environments. Whether you are producing automotive parts, functional prototypes, cosplay accessories, or detailed display models, this material combines strength with an attractive surface finish.
Description
The Anycubic PETG-CF Satin Carbon Fiber Filament is an excellent choice for makers looking to produce high-quality, durable prints with a professional finish. Carbon fiber reinforcement improves stiffness while maintaining the dependable printability associated with PETG. The refined satin texture helps hide layer lines, reducing post-processing while delivering attractive results straight from the printer. Part Number HTFBK-101 is ideal for users seeking reliable performance for both functional engineering projects and decorative creations.
Features
Built for Strength and Professional Results
Unlike standard PETG, this carbon fiber reinforced material is designed to withstand greater mechanical stress while maintaining excellent print quality. The satin finish enhances the visual appeal of every print, making it suitable for applications where both performance and appearance matter.
Ideal applications include:
- Functional prototypes and engineering parts
- Automotive components and accessories
- Sci-fi models and cosplay props
- Decorative functional items
- Toys and fandom creations
Printing Recommendations
For the best printing performance, ensure the filament is thoroughly dried before use. A hardened steel nozzle is recommended because of the abrasive carbon fiber content, helping maintain print quality and extend nozzle life.
Recommended settings:
- Printer technology: FDM (Fused Deposition Modeling)
- Filament type: PETG-CF
- Recommended nozzle size: 0.4 mm or larger
- Nozzle material: Hardened steel
- Printing temperature: 240 to 270 Degrees C
- Heated bed temperature: 65 to 70 Degrees C
- Recommended print speed: 40 to 250 mm/s
- Cooling time: 6 seconds
- Drying conditions: 60 to 65 Degrees C for 6 to 8 hours in a convection oven
- ACE compatible
- Intelligent filament identification supported
- Reusable filament spool supported
Material Performance
The carbon fiber blend provides an excellent balance of strength, rigidity, and durability while maintaining dependable PETG printability.
Key material properties:
- Colour: Black (#2D2926)
- Density: 1.32 g/cm3
- Maximum volume speed: 11 mm3/s
- Melt index: 14.1 +/- 1.6 g/10 min
- Melting point: 221 Degrees C
- Vicat softening temperature: 74 Degrees C
- Heat deflection temperature (0.45 MPa): 67 Degrees C
- Saturated water absorption: 0.38%
- Young's modulus: 2550 +/- 100 MPa
- Tensile strength: 54 +/- 2 MPa
- Tensile strength (Z): 37 +/- 3 MPa
- Elongation at break: 12 +/- 1%
- Bending modulus: 3100 +/- 150 MPa
- Bending strength: 88 +/- 2 MPa
- Izod impact strength (X-Y): 60 +/- 4 kJ/m2
Package Contents
- 1 x Anycubic PETG-CF Satin Carbon Fiber Filament 1kg Black
If you are looking for a premium carbon fiber reinforced PETG filament that combines outstanding mechanical strength with a refined satin finish, the Anycubic PETG-CF Satin Carbon Fiber Filament 1kg Black is an excellent solution. With Part Number HTFBK-101, it is well suited for demanding functional prints, detailed display pieces, and professional prototyping projects.
Specifications
| ©2026 Respective owners and brand holders. This table has been carefully researched and generated by ComXpert International CC (//www.comx-computers.co.za), however, errors and omissions may occur. Only references to South Africa apply. All products are sourced in South Africa from the official suppliers and the warranty is that of the local supplier. E&OE. This table and our site's content may be used on condition that this notice and link remains intact and unaltered. |
Specifications |
| Product Code | HTFBK-10 |
| Colour | Black (#2D2926) |
| Printer Technology | FDM (Fused Deposition Modeling) |
| Supporting Filaments | PETG-CF |
| Dry Out Before Use | Required |
| Drying Condition | Convection oven 60-65 degreesC, 6-8 h |
| ACE Compatibility | Compatible |
| Nozzle Size | Recommended 0.4 mm or above |
| Nozzle Material | Hardened steel |
| Printing Temperature | 240-270 degreesC |
| Heated Bed Temperature | 65-70 degreesC |
| Recommended Printing Speed | 40-250 mm/s |
| Cooling Time | 6 s |
| Maximum Volume Speed (Flow Rate) | 11 mm³/s |
| Density | 1.32 g/cm³ |
| Melt Index | 14.1±1.6 g/10 min (190degreesC/2.16kg) |
| Melting Point Temperature | 221 degreesC |
| Vicat Softening Temperature | 74 degreesC |
| Heat Deflection Temperature (0.45MPa) | 67 degreesC |
| Saturated Water Absorption Rate | 0.38% |
| Young's Modulus | 2550±100 Mpa |
| Tensile Strength | 54±2 Mpa |
| Elongation at Break | 12±1% |
| Bending Modulus | 3100±150 Mpa |
| Bending Strength | 88±2 MPa |
| lzod lmpact Strength (X-Y) | 60±4 kJ/m² |
| Tensile Strength (Z) | 37±3 MPa |
| Filament Type | Functional & Aesthetic filaments |
| Recommend to Print | Toys, functional decorative parts, and fandom |
| Intelligent Identification | Supported |
| Reusable Filament Spool | Supported |
Up
Down
Mobile store